Norbornene-substituted bisphenol antioxidants

ABSTRACT

The antioxidants of the formulae I and II ##STR1## in which R 1  is methyl or H, 
     R 2  is H or methyl, 
     R 3  is H or C 1  -C 4  alkyl, 
     R 4  is C 1  -C 5  alkyl, 
     R 5  is C 1  -C 5  alkyl, and the group Z is CH 2  or O, 
     are particularly suitable for stabilizing styrene (co)polymers.

The invention relates to compounds of the formulae I and II described below, to compositions comprising them, and to their use for stabilizing organic material.

The literature discloses norbornenes substituted with a phenol group (U.S. Pat. No. 4,301,306; U.S. Pat. No. 4,355,148).

EP 466 263 describes bisphenols, especially para-para bisphenols, which are substituted with a norbornene group, an example being the ##STR2## There continues to be a need for effective stabilizers for organic materials which are sensitive to thermal, oxidative or light-induced degradation.

Specific, norbornene-substituted bisphenols have now been found of the formulae I and II, ##STR3## in which R₁ is methyl or H, preferably H,

R₂ is H or methyl, preferably H,

R₃ is H or C₁ -C₄ alkyl, preferably H,

R₄ is C₁ -C₅ alkyl, preferably t-butyl,

R₅ is C₁ -C₅ alkyl, preferably methyl or t-butyl, and

the group Z is CH₂ or O, preferably CH₂.

The compounds are particularly suitable as antioxidants for styrene polymers.

Preference is given to compounds of the formula I or II in which

R₁ is H,

R₂ is H,

R₃ is H,

R₄ is t-butyl,

R₅ is methyl or t-butyl, and

the group Z is CH₂.

Particular preference is given to those compounds of the formulae I and II in which Z is CH₂ and/or R₁ is H.

Very particular preference is given to the compound ##STR4## Depending on the stated number of C atoms, alkyl is, for example, methyl, ethyl, n-propyl, isopropyl, n-, i-, sec- or t-butyl or pentyl.

The C atoms marked with * in the formulae are asymmetric C atoms. In general, this involves diastereoisomer mixtures (exo/endo) of the novel compounds. However, if required, the diastereoisomers can also be separated by known methods (for example by co-crystallization or chromatography). In the text below, the asymmetric C atoms are not marked.

A particular property of organic substances is that they readily undergo decomposition as a result of heat, light and/or radiation, mechanical stress (especially as a result of shear forces) and chemical reagents (especially atmospheric oxygen).

The compounds of the formula I and/or II are suitable for stabilizing organic material, especially polymers, specifically styrene (co)polymers, such as polystyrene, ABS (acrylonitrile-butadiene-styrene), IPS (impact polystyrene, graft copolymer of styrene on polybutadiene), MBS (methacrylonitrile-butadiene-styrene) and SBS (styrene-butadiene-styrene). In this context, they act in particular as antioxidants.

The invention therefore also relates to compositions comprising an organic material which is sensitive to oxidative, thermal and/or light-induced degradation, and at least one compound of the formula I and/or II.

In these compositions, the content of the novel compounds is expediently from 0.01 to 10% by weight, for example from 0.05 to 5% by weight, preferably from 0.05 to 3% by weight, but in particular from 0.1 to 2% by weight. One or more of these compounds may be present in such compositions, and the percentages by weight relate to the overall amount of these compounds. Here, the basis for calculation is the overall weight of the organic material without the compounds of the formulae I and II.

Examples of organic materials to be stabilized are:

1. Polymers of monoolefins and diolefins, for example polypropylene, polyisobutylene, polybut-1-ene, poly-4-methylpent-1-ene, polyisoprene or polybutadiene, as well as polymers of cycloolefins, for example of cyclopentene, norbornene or dicyclopentadiene; furthermore polyethylene (which optionally can be crosslinked), for example high density polyethylene (HDPE), low density polyethylene (LDPE), linear low density polyethylene (LLDPE), branched low density polyethylene (BLDPE).

Polyolefins, i.e. polymers of monoolefins exemplified in the preceding paragraph, in particular polyethylene and polypropylene, can be prepared by different, and especially by the following, methods:

a) radical polymerization (normally under high pressure and at elevated temperature)

b) catalytic polymerization using a catalyst that normally contains one or more metals of group IVb, Vb, VIb or VIII of the Periodic Table. These metals usually have one or more ligands, such as oxides, halides, alcoholates, esters, ethers, amines, alkyls, alkenyls and/or aryls that may be either π- or σ-coordinated. These metal complexes may be in the free form or fixed on substrates, for example on activated magnesium chloride, titanium(III) chloride, alumina or silicon oxide. These catalysts may be soluble or insoluble in the polymerization medium. The catalysts can be active as such in the polymerization or further activators may be used, for example metal alkyls, metal hydrides, metal alkyl halides, metal alkyl oxides or metal alkyloxanes, the metals being elements of groups Ia, IIa and/or IIIa of the Periodic Table. The activators may be modified, for example, with further ester, ether, amine or silyl ether groups. These catalyst systems are usually termed Phillips, Standard Oil Indiana, Ziegler (-Natta), TNZ (DuPont), metallocene or single site catalysts (SSC).

2. Mixtures of the polymers mentioned under 1), for example mixtures of polypropylene with polyisobutylene, polypropylene with polyethylene (for example PP/HDPE, PP/LDPE) and mixtures of different types of polyethylene (for example LDPE/HDPE).

3. Copolymers of monoolefins and diolefins with each other or with other vinyl monomers, for example ethylene-propylene copolymers, linear low density polyethylene (LLDPE) and mixtures thereof with low density polyethylene (LDPE), propylene-but-1-ene copolymers, propylene-isobutylene copolymers, ethyl-ene-but-1-ene copolymers, ethylene-hexene copolymers, ethylene-methylpentene copolymers, ethylene-heptene copolymers, ethylene-octene copolymers, propylene-butadiene copolymers, isobutylene-isoprene copolymers, ethylene-alkyl acrylate copolymers, ethylene-alkyl methacrylate copolymers, ethylene-vinyl acetate copolymers and their copolymers with carbon monoxide or ethylene-acrylic acid copolymers and their salts (ionomers) as well as terpolymers of ethylene with propylene and a diene such as hexadiene, dicyclopentadiene or ethylidene-norbornene; and mixtures of such copolymers with one another and with polymers mentioned under 1), for example polypropylene-ethylene-propylene copolymers, LDPE-ethylene-vinyl acetate copolymers, LDPE-ethylene-acrylic acid copolymers, LLDPE-ethylene-vinyl acetate copolymers, LLDPE-ethylene-acrylic acid copolymers and alternating or random polyalkylene-carbon monoxide copolymers and mixtures thereof with other polymers, for example polyamides.

4. Hydrocarbon resins (for example C₅ -C₉) including hydrogenated modifications thereof (e.g. tackifier resins) and mixtures of polyalkylenes and starch.

5. Polystyrene, poly(p-methylstyrene), poly(alpha-methylstyrene).

6. Copolymers of styrene or alpha-methylstyrene with dienes or acrylic derivatives, for example styrene-butadiene, styrene-acrylonitrile, styrene-alkyl methacrylate, styrene-butadiene-alkyl acrylate, styrene-butadiene-alkyl methacrylate, styrene-maleic anhydride, styrene-acrylonitrile-methyl acrylate; mixtures of high impact strength of styrene copolymers and another polymer, for example a polyacrylate, a diene polymer or an ethylene-propylene-diene terpolymer; and block copolymers of styrene such as styrene-butadiene-styrene (SBS), styrene-isoprene-styrene, styrene-ethylene-butylene-styrene or styrene-ethylene-propylene-styrene.

7. Graft copolymers of styrene or alpha-methylstyrene, for example styrene on polybutadiene, styrene on polybutadiene-styrene or polybutadiene-acrylonitrile copolymers, styrene and acrylonitrile (or methacrylonitrile) on polybutadiene; styrene, acrylonitrile and methyl methacrylate on polybutadiene; styrene and maleic anhydride on polybutadiene; styrene, acrylonitrile and maleic anhydride or maleimide on polybutadiene; styrene and maleimide on polybutadiene, styrene and alkyl acrylates or alkyl methacrylates on polybutadiene, styrene and acrylonitrile on ethylene-propylene-diene terpolymers, styrene and acrylonitrile on polyalkyl acrylates or polyalkyl methacrylates, styrene and acrylonitrile on acrylate-butadiene copolymers, as well as mixtures thereof with the copolymers mentioned under 6), for example the copolymer mixtures known as ABS, MBS, ASA or AES polymers.

8. Halogen-containing polymers such as polychloroprene, chlorinated rubber, chlorinated or sulfochlorinated polyethylene, copolymers of ethylene and chlorinated ethylene, epichlorohydrin homo- and copolymers, especially polymers of halogen-containing vinyl compounds, for example polyvinyl chloride, polyvinylidene chloride, polyvinyl fluoride, polyvinylidene fluoride; as well as copolymers thereof such as vinyl chloride-vinylidene chloride, vinyl chloride-vinyl acetate or vinylidene chloride-vinyl acetate.

9. Polymers derived from alpha,beta-unsaturated acids and derivatives thereof such as polyacrylates and polymethacrylates, polymethyl methacrylates, polyacrylamides and polyacrylonitriles, impact-modified with butyl acrylate.

10. Copolymers of the monomers mentioned under 9) with each other or with other unsaturated monomers, for example acrylonitrile-butadiene copolymers, acrylonitrile-alkyl acrylate copolymers, acrylonitrile-alkoxyalkyl acrylate copolymers, acrylonitrile-vinyl halide copolymers or acrylonitrile-alkyl methacrylate-butadiene terpolymers.

11. Polymers derived from unsaturated alcohols and amines or the acyl derivatives or acetals thereof, such as polyvinyl alcohol, polyvinyl acetate, polyvinyl stearate,polyvinyl benzoate, polyvinyl maleate, polyvinyl butyral, polyallyl phthalate or polyallylmelamine; as well as their copolymers with olefins mentioned in point 1.

12. Homopolymers and copolymers of cyclic ethers such as polyalkylene glycols, polyethylene oxide, polypropylene oxide or copolymers thereof with bisglycidyl ethers.

13. Polyacetals such as polyoxymethylene and those polyoxymethylenes which contain comonomers, for example ethylene oxide; polyacetals modified with thermoplastic polyurethanes, acrylates or MBS.

14. Polyphenylene oxides and sulfides, and mixtures thereof with styrene polymers or polyamides.

15. Polyurethanes derived from hydroxyl-terminated polyethers, polyesters and polybutadienes on the one hand and aliphatic or aromatic polyisocyanates on the other, as well as precursors thereof.

16. Polyamides and copolyamides derived from diamines and dicarboxylic acids and/or from aminocarboxylic acids or the corresponding lactams, such as polyamide 4, 6, 6/6, 6/10, 6/9, 6/12, 4/6, 12/12, 11 and 12, aromatic polyamides starting from m-xylene, diamine and adipic acid; polyamides prepared from hexamethylenediamine and isophthalic and/or terephthalic acid and with or without an elastomer as modifier, for example poly-2,4,4-trimethylhexamethylene terephthalamide or poly-m-phenylene isophthalamide. Block copolymers of the aforementioned polyamides with polyolefins, olefin copolymers, ionomers or chemically bonded or grafted elastomers; or with polyethers, e.g. with polyethylene glycol, polypropylene glycol or polytetramethylene glycol. As well as polyamides or copolyamides modified with EPDM or ABS; and polyamides condensed during processing (RIM polyamide systems).

17. Polyureas, polyimides, polyamide-imides and polybenzimidazoles.

18. Polyesters derived from dicarboxylic acids and dialcohols and/or from hydroxycarboxylic acids or the corresponding lactones, such as polyethylene terephthalate, polybutylene terephthalate, poly-1,4-dimethylolcyclohexane terephthalate, polyhydroxybenzoates, as well as block polyether esters derived from hydroxyl-terminated polyethers; and also polyesters modified with polycarbonates or MBS.

19. Polycarbonates and polyester carbonates.

20. Polysulfones, polyether sulfones and polyether ketones.

21. Crosslinked polymers derived from aldehydes on the one hand and phenols, urea or melamine on the other hand, such as phenol/formaldehyde resins, urea/formaldehyde resins and melamine/formaldehyde resins.

22. Drying and non-drying alkyd resins.

23. Unsaturated polyester resins derived from copolyesters of saturated and unsaturated dicarboxylic acids with polyhydric alcohols and vinyl compounds as crosslinking agents, and also halogen-containing modifications thereof of low flammability.

24. Crosslinkable acrylic resins derived from substituted acrylates, for example from epoxy acrylates, urethane acrylates or polyester acrylates.

25. Alkyd resins, polyester resins and acrylate resins crosslinked with melamine resins, urea resins, polyisocyanates or epoxy resins.

26. Crosslinked epoxy resins derived from polyepoxides, for example from bisglycidyl ethers, or cycloaliphatic diepoxides.

27. Natural polymers such as cellulose, natural rubber, gelatin and derivatives thereof which have been chemically modified in a polymer-homologous manner, for example cellulose acetates, cellulose propionates and cellulose butyrates, or the cellulose ethers such as methylcellulose; and also rosins and derivatives.

28. Blends (polyblends) of the aforementioned polymers, for example PP/EPDM, polyamide/EPDM or ABS, PVC/EVA, PVC/ABS, PVC/MBS, PC/ABS, PBTP/ABS, PC/ASA, PC/PBT, PVC/CPE, PVC/acrylates, POM/thermoplastic PUR, PC/thermoplastic PUR, POM/acrylate, POM/MBS, PPO/HIPS, PPO/PA 6.6 and copolymers, PA/HDPE, PA/PP or PA/PPO.

29. Aqueous emulsions of natural or synthetic rubbers, for example natural rubber latex or latices of carboxylated styrene-butadiene copolymers.

30. Natural and synthetic organic substances which are pure monomeric compounds or mixtures thereof, for example mineral oils, animal or vegetable fats, oils and waxes, or oils, waxes and fats based on synthetic esters (e.g. phthalates, adipates, phosphates or trimellitates), and also blends of synthetic esters with mineral oils in any desired proportions by weight, as are employed, for example, as spin finishes, and also the aqueous emulsions thereof.

Among these, substances having double bonds are preferred, since it is thereby possible to utilize the advantage of chemical incorporation into the substrate.

Examples of such substrates are elastomers. Suitable examples of these are:

1. Polydienes, for example polybutadiene, polyisoprene or polychloroprene; block copolymers, for example styrene-butadiene-styrene, styrene-isoprene-styrene or acrylonitrile-butadiene copolymers.

2. Copolymers of mono- and diolefins with each other or with other vinyl monomers, for example ethylene-alkyl acrylate copolymers, ethylene-alkyl methacrylate copolymers, ethylene-vinyl acetate copolymers and also terpolymers of ethylene with propylene and a diene such as hexadiene, dicyclopentadiene or ethylidenenorbornene.

3. Halogen-containing polymers, for example polychloroprene, chlorinated rubber, chlorinated or sulfochlorinated polyethylene, epichlorohydrin homo- and copolymers, chlorotrifluoroethylene copolymers, polymers of halogen-containing vinyl compounds, for example polyvinylidene chloride, polyvinylidene fluoride; and copolymers thereof, such as vinyl chloride-vinylidene chloride, vinyl chloride-vinyl acetate or vinylidene chloride-vinyl acetate.

4. Polyurethanes, derived from hydroxyl-terminated polyethers, polyesters and polybutadiene on the one hand and from aliphatic or aromatic polyisocyanates on the other hand, and their precursors.

5. Natural rubber.

6. Blends (polyblends) of the abovementioned polymers.

7. Aqueous emulsions of natural or synthetic rubbers, such as natural rubber latex or latices of carboxylated styrene-butadiene copolymers.

These elastomers may be present in the form of latices and can be stabilized as such. It is also possible to stabilize vulcanizates.

Preferred compositions are those including as elastomer a polydiene, such as polybutadiene rubber.

Incorporation into the organic materials can be carried out, for example, by mixing in the novel compounds or mixtures and, if desired, further additives in accordance with the methods customary in the art. Where polymers are concerned, especially synthetic polymers, incorporation can take place prior to or during the shaping operation or by applying the dissolved or dispersed compounds to the polymer, with or without subsequent evaporation of the solvent. In the case of elastomers, these can also be stabilized as latices. A further, preferred possibility for use of the novel compounds is their addition, during the preparation of rubber mixtures, together with the other, customary mixture constituents and ingredients in accordance with the customary techniques, for example in Banbury mixers, on mixing-roll units or in mixing extruders.

In particular, the presence of the compounds of the formula I and/or II during the mixing process, as well as during subsequent shaping and the crosslinking reaction (vulcanization to give the finished rubber article) and during use of the finished article, brings about chemical linking with the elastomer/polymer. This can be determined, for example, analytically by the high residual content of additive--measured on the basis of the residual nitrogen--in comparison with compounds which cannot be incorporated.

The invention therefore relates in particular to compositions in which compounds of the formula I and/or II are incorporated into and/or chemically linked with an elastomer/polymer.

The novel compounds or mixtures can also be added in the form of a master batch, which contains these compounds in a concentration, for example, of from 2.5 to 25% by weight, to the plastics which are to be stabilized.

The compounds of the formulae I and II can expediently be incorporated by the following methods:

as emulsion or dispersion (e.g. to latices or emulsion polymers)

as a dry mix during the mixing in of additional components or polymer mixtures

by direct addition to the processing apparatus (e.g. extruder, internal mixer, etc.)

as a solution or melt.

Novel polymer compositions can be employed in various forms and processed to give various products, for example as or to films, fibres, tapes, moulding compounds or profiles, or as binders for coating materials, adhesives or putties.

In addition to the novel compounds and/or mixtures, the novel compositions can also--and especially if they include organic, preferably synthetic, polymers--comprise further customary additives known to the skilled worker, for example:

1. Antioxidants

1.1. Alkylated monophenols, for example 2,6-di-tert-butyl-4-methylphenol, 2-butyl-4,6-dimethylphenol, 2,6-di-tert-butyl-4-ethylphenol, 2,6-di-tert-butyl-4-n-butylphenol, 2,6-di-tert-butyl-4-isobutylphenol, 2,6-dicyclopentyl-4-methylphenol, 2-(a-methylcyclohexyl)-4,6-dimethylphenol, 2,6-dioctadecyl-4-methylphenol, 2,4,6-tricyclohexylphenol, 2,6-di-tert-butyl-4-methoxymethylphenol, 2,6-di-nonyl-4-methylphenol, 2,4-dimethyl-6-(1'-methylundec-1'-yl)-phenol, 2,4-dimethyl-6-(1'-methylheptadec-1'-yl)phenol, 2,4-dimethyl-6-(1'-methyl-tridec-1'-yl)phenol and mixtures thereof.

1.2. Alkylthiomethylphenols, for example 2,4-dioctylthiomethyl-6-tert-butylphenol, 2,4-dioctylthiomethyl-6-methylphenol, 2,4-dioctylthiomethyl-6-ethylphenol, 2,6-didodecylthiomethyl-4-nonylphenol.

1.3. Hydroquinones and alkylated hydroquinones, for example 2,6-di-tert-butyl-4-methoxyphenol, 2,5-di-tert-butylhydroquinone, 2,5-di-tert-amylhydroquinone, 2,6-diphenyl-4-octadecyloxyphenol, 2,6-di-tert-butylhydroquinone, 2,5-di-tert-butyl-4-hydroxyanisole, 3,5-di-tert-butyl-4-hydroxyanisole, 3,5-di-tert-butyl-4-hydroxyphenyl stearate, bis(3,5-di-tert-butyl-4-hydroxyphenyl) adipate.

1.4. Tocopherols, for example α-tocopherol, β-tocopherol, γ-tocopherol, δ-tocopherol and mixtures thereof (vitamin E).

1.5 Hydroxylated thiodiphenyl ethers, for example 2,2'-thiobis(6-tert-butyl-4-methylphenol), 2,2'-thiobis(4-octylphenol), 4,4'-thiobis(6-tert-butyl-3-methylphenol), 4,4'-thiobis(6-tert-butyl-2-methylphenol), 4,4'-thiobis(3,6-di-sec.-amylphenol), 4,4'-bis(2,6-dimethyl-4-hydroxyphenyl)disulfide.

1.6. Alkylidenebisphenols, for example 2,2'-methylenebis(6-tert-butyl-4-methylphenol), 2,2'-methylenebis(6-tert-butyl-4-ethylphenol), 2,2'-methylenebis 4-methyl-6-(alpha-methylcyclohexyl)-phenol!, 2,2'-methylenebis(4-methyl-6-cyclohexylphenol), 2,2'-methylenebis(6-nonyl-4-methylphenol), 2,2'-methylenebis(4,6-di-tert-butylphenol), 2,2'-ethylidenebis(4,6-di-tert-butylphenol), 2,2'-ethylidenebis(6-tert-butyl-4-isobutylphenol), 2,2'-methylenebis 6-(alpha-methylbenzyl)-4-nonylphenol!, 2,2'-methylenebis 6-(alpha,alpha-dimethylbenzyl)-4-nonylphenol!, 4,4'-methylenebis(2,6-di-tert-butylphenol), 4,4'-methylenebis(6-tert-butyl-2-methylphenol), 1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 2,6-bis(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methylphenol, 1,1,3-tris(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)-3-n-dodecylmercaptobutane, ethylene glycol bis 3,3-bis(3'-tert-butyl-4'-hydroxyphenyl)butyrate!, bis(3-tert-butyl-4-hydroxy-5-methylphenyl)dicyclopentadiene, bis 2-(3'-tert-butyl-2'-hydroxy-5'-methylbenzyl)-6-tert-butyl-4-methylphenyl! terephthalate, 1,1-bis(3,5-dimethyl-2-hydroxyphenyl)butane, 2,2-bis(3,5-di-tert-butyl-4-hydroxyphenyl)propane, 2,2-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)-4-n-dodecylmercaptobutane, 1,1,5,5-tetra(5-tert-butyl-4-hydroxy-2-methyl phenyl)pentane.

1.7. O--, N-- and S-benzyl compounds, for example 3,5,3',5'-tetra-tert-butyl-4,4'-dihydroxydibenzyl ether, octadecyl 4-hydroxy-3,5-dimethylbenzylmercaptoacetate, tris(3,5-di-tert-butyl-4-hydroxybenzyl)amine, bis(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl) dithioterephthalate, bis(3,5-di-tert-butyl-4-hydroxybenzyl) sulfide, isooctyl 3,5-di-tert-butyl-4-hydroxybenzylmercaptoacetate.

1.8. Hydroxybenzylated malonates, for example dioctadecyl 2,2-bis(3,5-di-tert-butyl-2-hydroxybenzyl)malonate, dioctadecyl 2-(3-tert-butyl-4-hydroxy-5-methylbenzyl)malonate, di-dodecyl mercaptoethyl-2,2-bis(3,5-di-tert-butyl-4-hydroxybenzyl)malonate, di- 4-(1,1,3,3-tetramethylbutyl)phenyl!2,2-bis(3,5-di-tert-butyl-4-hydroxybenzyl)malonate.

1.9. Aromatic hydroxybenzyl compounds, for example 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene, 1,4-bis(3,5-di-tert-butyl-4-hydroxybenzyl)-2,3,5,6-tetramethylbenzene, 2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)phenol.

1.10. Triazine compounds, for example 2,4-bisoctylmercapto-6-(3,5-di-tert-butyl-4-hydroxyanilino)-1,3,5-triazine, 2-octylmercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxyanilino)-1,3,5-triazine, 2-octylmercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxyphenoxy)-1,3,5-triazine, 2,4,6-tris(3,5-di-tert-butyl-4-hydroxyphenoxy)-1,2,3-triazine, 1 ,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl) isocyanurate, 1,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl) isocyanurate, 2,4,6-tris(3,5-di-tert-butyl-4-hydroxyphenylethyl)-1,3,5-triazine, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hexahydro-1,3,5-triazine, 1,3,5-tris(3,5-dicyclohexyl-4-hydroxybenzyl) isocyanurate.

1.11. Benzylphosphonates, for example dimethyl 2,5-di-tert-butyl-4-hydroxybenzyl-phosphonate, diethyl 3,5-di-tert-butyl-4-hydroxybenzylphosphonate, dioctadecyl 3,5-di-tert-butyl-4-hydroxybenzylphosphonate, dioctadecyl 5-tert-butyl-4-hydroxy-3-methylbenzylphosphonate, the calcium salt of the monoethyl ester of 3,5-di-tert-butyl-4-hydroxybenzylphosphonic acid.

1.12. Acylaminophenols, for example 4-hydroxylauranilide, 4-hydroxystearanilide, octyl N-(3,5-di-tert-butyl-4-hydroxyphenyl)carbamate.

1.13. Esters of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid with mono- or polyhydric alcohols, e.g. with methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tris(hydroxyethyl) isocyanurate, N,N'-bis(hydroxyethyl)oxalamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo 2.2.2!octane.

1.14. Esters of beta-(5-tert-butyl-4-hydroxy-3-methylphenyl)propionic acid with mono- or polyhydric alcohols, e.g. with methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tris(hydroxy)ethyl isocyanurate, N,N'-bis(hydroxyethyl)oxalamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo 2.2.2!octane.

1.15. Esters of beta-(3,5-dicyclohexyl-4-hydroxyphenyl)propionic acid with mono- or polyhydric alcohols, e.g. with methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tris(hydroxy)ethyl isocyanurate, N,N'-bis(hydroxyethyl)oxalamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo 2.2.2!octane.

1.16. Esters of 3,5-di-tert-butyl-4-hydroxyphenyl acetic acid with mono- or polyhydric alcohols, e.g. with methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tris(hydroxy)ethyl isocyanurate, N,N'-bis-(hydroxyethyl)oxalamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo 2.2.2!octane.

1.17. Amides of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid e.g. N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hexamethylenediamine, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)trimethylenediamine, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hydrazine.

2. UV absorbers and light stabilizers

2.1. 2-(2'-Hydroxyphenyl)benzotriazoles, for example 2-(2'-hydroxy-5'-methylphenyl)-benzotriazole, 2-(3',5'-di-tert-butyl-2'-hydroxyphenyl)benzotriazole, 2-(5'-tert-butyl-2'-hydroxyphenyl)benzotriazole, 2-(2'-hydroxy-5'-(1,1,3,3-tetramethylbutyl) phenyl)-benzotriazole, 2-(3',5'-di-tert-butyl-2'-hydroxyphenyl)-5-chlorobenzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-methylphenyl)-5-chlorobenzotriazole, 2-(3'-sec-butyl-5'-tert-butyl-2'-hydroxyphenyl)benzotriazole, 2-(2'-hydroxy-4'-octoxyphenyl)benzotriazole, 2-(3',5'-di-tert-amyl-2'-hydroxyphenyl)benzotriazole, 2-(3',5'-bis(alpha,alpha-dimethylbenzyl)-2'-hydroxyphenyl)-benzotriazole, a mixture of 2-(3'-tert-butyl-2'-hydroxy-5'-(2-octyloxycarbonylethyl)phenyl)-5-chlorobenzotriazole, 2-(3'-tert-butyl-5'- 2-(2-ethyl hexyloxy)carbonylethyl!-2'-hydroxyphenyl)-5-chlorobenzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-methoxycarbonylethyl)phenyl)-5-chlorobenzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-methoxycarbonylethyl) phenyl)-benzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-octyloxycarbonylethyl)phenyl)benzotriazole, 2-(3'-tert-butyl-5'- 2-(2-ethylhexyloxy)carbonylethyl!-2'-hydroxyphenyl)benzotriazole, 2-(3'-dodecyl-2'-hydroxy-5'-methylphenyl)benzotriazole, and 2-(3'-tert-butyl-2'-hydroxy-5'-(2-isooctyloxycarbonylethyl)phenyl)benzotriazole, 2,2'-methylenebis 4-(1,1,3,3-tetramethylbutyl)-6-benzotriazol-2-ylphenol!; the transesterification product of 2- 3'-tert-butyl-5'-(2-methoxy-carbonylethyl)-2'-hydroxyphenyl!benzotriazole with polyethylene glycol 300; ##STR5## where R=3'-tert-butyl-4'-hydroxy-5'-2H-benzotriazol-2-ylphenyl.

2.2. 2-Hydroxybenzophenones, for example the 4-hydroxy, 4-methoxy, 4-octoxy, 4-decyloxy, 4-dodecyloxy, 4-benzyloxy, 4,2',4'-trihydroxy and 2'-hydroxy-4,4'-dimethoxy derivative.

2.3. Esters of substituted or unsubstituted benzoic acids, for example 4-tert-butyl-phenyl salicylate, phenyl salicylate, octylphenyl salicylate, dibenzoylresorcinol, bis(4-tert-butylbenzoyl)resorcinol, benzoylresorcinol, 2,4-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzoate, hexadecyl 3,5-di-tert-butyl-4-hydroxybenzoate, octadecyl 3,5-di-tert-butyl-4-hydroxybenzoate, 2-methyl-4,6-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzoate.

2.4. Acrylates, for example ethyl alpha-cyano-beta,beta-diphenylacrylate or isooctyl alpha-cyano-β,β-diphenylacrylate, methyl α-carbomethoxycinnamate, methyl alpha-cyano-beta-methyl-p-methoxy-cinnamate or butyl α-cyano-β-methyl-p-methoxycinnamate, methyl alpha-carbomethoxy-p-methoxycinnamate and N-(beta-carbomethoxy-beta-cyanovinyl)-2-methylindoline.

2.5. Nickel compounds, for example nickel complexes of 2,2'-thiobis 4-(1,1,3,3-tetramethylbutyl)phenol!, such as the 1:1 or 1:2 complex, with or without additional ligands such as n-butylamine, triethanolamine or N-cyclohexyldiethanolamine, nickel dibutyldithiocarbamate, nickel salts of monoalkyl esters, such as of the methyl or ethyl ester, of 4-hydroxy-3,5-di-tert-butylbenzylphosphonic acid, nickel complexes of ketoximes, e.g. of 2-hydroxy-4-methylphenyl undecyl ketoxime, nickel complexes of 1-phenyl-4-lauroyl-5-hydroxypyrazole, with or without additional ligands.

2.6. Sterically hindered amines, for example bis(2,2,6,6-tetramethylpiperidyl) sebacate, bis(2,2,6,6-tetramethylpiperidyl) succinate, bis(1,2,2,6,6-pentamethylpiperidyl) sebacate, bis(1,2,2,6,6-pentamethylpiperidyl) n-butyl 3,5-di-tert-butyl-4-hydroxybenzylmalonate, the condensate of 1-hydroxyethyl-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, the condensate of N,N'-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-tert-octylamino-2,6-dichloro-1,3,5-s-triazine, tris(2,2,6,6-tetramethyl-4-piperidyl) nitrilotriacetate, tetrakis(2,2,6,6-tetramethyl-4-piperidyl) 1,2,3,4-butanetetraoate, 1,1'-(1,2-ethanediyl)bis(3,3,5,5-tetramethylpiperazinone), 4-benzoyl-2,2,6,6-tetramethylpiperidine, 4-stearyloxy-2,2,6,6-tetramethylpiperidine, bis(1,2,2,6,6-pentamethylpiperidyl)-2-n-butyl-2-(2-hydroxy-3,5-di-tert-butylbenzyl) malonate, 3-n-octyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro 4.5!decane-2,4-dione, bis(1-octyloxy-2,2,6,6-tetramethylpiperidyl) sebacate, bis(1-octyloxy-2,2,6,6-tetramethylpiperidyl) succinate, the condensate of N,N'-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-morpholino-2,6-dichloro-1,3,5-triazine, the condensate of 2-chloro-4,6-di(4-n-butylamino-2,2,6,6-tetramethylpiperidyl)-1,3,5-triazine and 1,2-bis(3-aminopropylamino)ethane, the condensate of 2-chloro-4,6-di(4-n-butylamino-1,2,2,6,6-pentamethylpiperidyl)-1,3,5-triazine and 1,2-bis(3-aminopropylamino)ethane, 8-acetyl-3-dodecyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro 4. 5!decane-2,4-dione, 3-dodecyl-1-(2,2,6,6-tetramethyl-4-piperidyl)pyrrolidine-2,5-dione, 3-dodecyl-1-(1,2,2,6,6-pentamethyl-4-piperidyl)pyrrolidine-2,5-dione.

2.7. Oxalamides, for example 4,4'-dioctyloxyoxanilide, 2,2'-diethoxy-oxanilide, 2,2'-dioctyloxy-5,5'-di-tert-butyloxanilide, 2,2'-dioctyloxy-5,5'-di-tert-butyloxanilide, 2,2'-didodecyloxy-5,5'-di-tert-butyloxanilide, 2-ethoxy-2'-ethyloxanilide, N,N'-bis(3-dimethylaminopropyl)oxalamide, 2-ethoxy-5-tert-butyl-2'-ethyloxanilide and its mixture with 2-ethoxy-2'-ethyl-5,4'-di-tert-butyloxanilide and mixtures of o- and p-methoxy- and of o- and p-ethoxy-disubstituted oxanilides.

2.8. 2-(2-Hydroxyphenyl)-1,3,5-triazines, for example 2,4,6-tris(2-hydroxy-4-octyloxyphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2,4-dihydroxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2,4-bis(2-hydroxy-4-propoxyphenyl)-6-(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6bis(4-methylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-dodecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2- 2-hydroxy-4-(2-hydroxy-3-butyloxypropyloxy)phenyl!-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2- 2-hydroxy-4-(2-hydroxy-3-octyloxypropoxy)-phenyl!-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine.

3. Metal deactivators, for example N,N'-diphenyloxalamide, N-salicylal-N'-salicyloyl hydrazine, N,N'-bis(salicyloyl)hydrazine, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenyl-propionyl)hydrazine, 3-salicyloylamino-1,2,4-triazole, bis(benzylidene)oxalyl dihydrazide, oxanilide, isophthaloyl dihydrazide, sebacoyl bisphenylhydrazide, N,N'-diacetyladipoyl dihydrazide, N,N'-bis(salicyloyl)oxalyl dihydrazide, N,N'-bis(salicyloyl)thiopropionyl dihydrazide.

4. Phosphites and phosphonites, for example triphenyl phosphite, diphenyl alkyl phosphites, phenyl dialkyl phosphites, tris(nonylphenyl) phosphite, trilauryl phosphite, trioctadecyl phosphite, distearyl pentaerythritol diphosphite, tris(2,4-di-tert-butylphenyl) phosphite, diisodecyl pentaerythritol diphosphite, bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, bis(2,6-di-tert-butyl-4-methylphenyl)pentaerythritol diphosphite, bisisodecyloxypentaerythritol diphosphite, bis(2,4-di-tert-butyl-6-methylphenyl)pentaerythritol diphosphite, bis-(2,4,6-tri-tert-butylphenyl)pentaerythritol diphosphite, tristearyl sorbitol triphosphite, tetrakis(2,4-di-tert-butylphenyl) 4,4'-biphenylene diphosphonite, 6-isooctyloxy-2,4,8,10-tetra-tert-butyl-12H-dibenzo d,g!-1,3,2-dioxaphosphocin, 6-fluoro-2,4,8,10-tetra-tert-butyl-12-methyl-dibenzo d,g!-1,3,2-dioxaphosphocin, bis(2,4-di-tert-butyl-6-methylphenyl) methyl phosphite, bis(2,4-di-tert-butyl-6-methylphenyl) ethyl phosphite.

5. Peroxide scavengers, for example esters of beta-thiodipropionic acid, for example the lauryl, stearyl, myristyl or tridecyl esters, mercaptobenzimidazole, the zinc salt of 2-mercaptobenzimidazole, zinc dibutyldithiocarbamate, dioctadecyl disulfide, pentaerythritol tetrakis(beta-dodecylmercapto)propionate.

6. Polyamide stabilizers, for example copper salts in combination with iodides and/or phosphorus compounds and salts of divalent manganese.

7. Basic co-stabilizers, for example melamine, polyvinylpyrrolidone, dicyandiamide, triallyl cyanurate, urea derivatives, hydrazine derivatives, amines, polyamides, polyurethanes, alkali metal salts and alkaline earth metal salts of higher fatty acids, for example calcium stearate, zinc stearate, magnesium behenate, magnesium stearate, sodium ricinoleate, potassium palmitate, antimony pyrocatecholate or tin pyrocatecholate.

8. Nucleating agents, for example 4-tert-butylbenzoic acid, adipic acid, diphenylacetic acid.

9. Fillers and reinforcing agents, for example calcium carbonate, silicates, glass fibres, asbestos, talc, kaolin, mica, barium sulfate, metal oxides and hydroxides, carbon black, graphite.

10. Other additives, for example plasticizers, lubricants, emulsifiers, pigments, optical brighteners, flameproofing agents, antistatic agents, blowing agents.

11. Benzofuranones and indolinones, for example those described in U.S. Pat. No. 4,325,863 or U.S. Pat. No. 4,338,244, U.S. Pat. No. 5,175,312, U.S. Pat. No. 5, 216,052, U.S. Pat. No. 5,252,643, DE-A-4 316 611, DE-A-4 316 622, DE-A-4 316 876, EP-A-0 589 839 or EP-A-0 591 102, or 3- 4-(2-acetoxyethoxy)phenyl!-5,7-di-tert-butyl-benzofuran-2-one, 5,7-di-tert-butyl-3- 4-(2-stearoyloxyethoxy)phenyl!-benzofuran-2-one, 3,3'-bis 5,7-di-tert-butyl-3-(4- 2-hydroxyethoxy!phenyl)-benzofuran-2-one!, 5,7-di-tert-butyl-3-(4-ethoxyphenyl)benzofuran-2-one, 3-(4-acetoxy-3,5-dimethylphenyl)-5,7-di-tert-butyl-benzofuran-2-one and 3-(3,5-dimethyl-4-pivaloyloxyphenyl)-5,7-di-tert-butyl-benzofuran-2-one.

The invention additionally relates to the use of compounds of the formulae I and II for stabilizing organic material against oxidative, thermal and/or actinic degradation.

Preference is given to the use of compounds of the formulae I and II as stabilizers in synthetic, natural or semisynthetic polymers.

The invention consequently also consists in a method of stabilizing organic material, especially natural, synthetic or semisynthetic polymers, which comprises adding or applying compounds of the formulae I and/or II as stabilizers to this material.

The compounds of the formulae I and/or II can be prepared by or in analogy to known methods. Condensing, for example, the bicyclic aldehyde III with an alkylated phenol IVa or IVb, respectively, ##STR6## gives the compounds of the formulae I and II. Condensation takes place as described, for example, in EP 466 263 and can be catalysed with an appropriate base, such as KOH or NaOH. In this reaction the molar ratio of IVa(b) to III is expediently 2:1.

A further possibility is catalysis with Bronsted or Lewis acids, for example H₂ SO₄, HCOOH, BF₃ or p-toluenesulfonic acid.

The examples which follow illustrate the invention in more detail. In the examples, the rest of the description and the claims the parts and percentages used are by weight unless stated otherwise.

EXAMPLE 1 ##STR7##

243.09 g (1.48 mol) of 2-t-butyl-6-methylphenol are added with cooling and under N₂ to a solution of 83.03 g (1.48 mol) of KOH in 1.2 l of MeOH. Then 90.41 g (0.74 mol) of norbornene-5-aldehyde in 300 ml of MeOH are added dropwise. The mixture is heated under reflux for 16 h and then brought to a pH of 6 with 110 ml of concentrated HCl. Working up by filtration, washing, drying over MgSO₄ and evaporation of the solvent gives 91.0 g (28.4% of theory ) of the above compound, which is recrystallized from hexane.

m.p. 156° C.

Analysis: calc. (found): C 83.28 (83.14) H 9.32 (9.44)

Use Example: Stabilization of acrylonitrile-butadiene-styrene (ABS) terpolymer -thermogravimetric test 1000 parts of unstabilized ABS powder (polybutadienes ˜25%) are mixed thoroughly with 100 parts of cyclohexane containing 2.5 parts of the stabilizer specified in Table I. The solvent is removed in vacuo at 40° C./N₂.

In a Mettler DTA2000 apparatus for thermogravimetric measurements, the temperature dependency of the oxidation of 5 g of stabilized ABS powder in an aluminium boat in a stream of oxygen (50 ml/min) at 180° C. is determined.

A characteristic temperature change is observed when the exothermic degradation reaction of the polymer begins. The time t until the exothermic reaction reaches a maximum is a measure of the thermal stability of the polymer. The longer this time, the better the thermal stability.

The results presented in Table I below show the superiority of the novel compound over the compound bisphenol N.

                  TABLE I                                                          ______________________________________                                         Compound       Concentration                                                                             t  min!                                              ______________________________________                                         Ex. 1          0.25%      56                                                   Bisphenol N.sup.1) :                                                                          0.25%      24                                                   ______________________________________                                          .sup.1) Compound of EP 466 263, Ex. 1, of the formula                          ##STR8##                                                                  

What is claimed is:
 1. The compound of the formula: ##STR9##
 2. A composition comprising an organic material sensitive to oxidative, thermal and/or light-induced degradation, and the compound according to claim
 1. 3. A composition according to claim 2, wherein the organic material is an organic, synthetic polymer.
 4. A composition according to claim 3, wherein the organic material is a styrene (co)polymer.
 5. A method of stabilizing organic material sensitive to oxidative, thermal and/or light-induced degradation, which comprises adding the compound according to claim 1 to this material.
 6. A method according claim 5, where the organic material is a polymer.
 7. A method according to claim 6, where the organic material is a styrene polymer or styrene copolymer. 